product features:
Rated voltage: 300/300V
Rated temperature: -60℃~+180℃
Conductor: N2GFAF tinned soft wire
N2GFA tinned single brass wire
Insulator: silicone rubber
Applicable for high temperature environment such as electrical household appliance, lamps and Lanterns, electrical equipment and electrical motors
wire print:
N2GFAF(N2GFA) 1×0.75mm² 180℃ 300/300V HUA CHENG CABLE NO.40013391
SIF(SIE) (1×0.25mm² 1×0.5mm² 1×1.0mm² 1×1.5mm² 1×2.5mm²) 180℃300/300V HUA CHENG CABLE
|
Items
|
Technical datas
|
Applied standard
|
|
Outer appearance
|
Smooth, even, without loose
|
DIN VDE 0250-502
DIN VDE 0282-1:1999.01
DIN VDE 0282-2:1999.01
|
|
Spark test
|
AC6KV/ 0.15 S
|
|
Vol. test
|
2 KV/5 min
|
|
Insulate Mechanical
characters
|
Before aging
|
Tensile strength
|
≥5.0N/mm²
|
|
Break elongation rate
|
≥150%
|
|
After aging
|
Tensile strength
|
≥4.0N/mm²
|
|
(200±3℃×240h)
|
Break elongation rate
|
≥120%
|
|
Poisonous substance control
|
Comply with ROHS rule
|
EU—2002/95/EC
|
|
N2GFAF(N2GFA)
|
|
|
TYPE
|
spec.
|
Conductor
|
Insulation
|
wire OD
|
Conductor Resistance
|
|
Structure
|
OD
|
Nominal Thickness
|
Min. Diameter
|
Nominal Diameter
|
Allowance
|
Ω/KM
|
|
mm²
|
No./mm
|
mm
|
mm
|
mm
|
mm
|
mm
|
below
|
|
SIF
|
0.25
|
8/0.20
|
0.65
|
0.60
|
0.44
|
1.85
|
±0.10
|
80.9
|
|
SIF
|
0.50
|
16/0.20
|
0.95
|
0.60
|
0.44
|
2.15
|
±0.10
|
40.1
|
|
N2GFAF
|
0.75
|
24/0.20
|
1.15
|
0.60
|
0.44
|
2.35
|
±0.10
|
26.7
|
|
SIF
|
1.0
|
32/0.20
|
1.34
|
0.60
|
0.44
|
2.55
|
±0.10
|
20.0
|
|
SIF
|
1.5
|
30/0.25
|
1.60
|
0.70
|
0.53
|
3.00
|
±0.15
|
13.7
|
|
SIF
|
2.5
|
49/0.25
|
2.00
|
0.80
|
0.62
|
3.60
|
±0.15
|
8.21
|
|
|
|
|
|
|
|
|
|
|
|
SIE
|
0.25
|
1/0.56
|
0.56
|
0.60
|
0.44
|
1.80
|
±0.10
|
76.0
|
|
SIE
|
0.50
|
1/0.80
|
0.80
|
0.60
|
0.44
|
2.00
|
±0.10
|
36.7
|
|
N2GFA
|
0.75
|
1/0.98
|
0.98
|
0.60
|
0.44
|
2.20
|
±0.10
|
24.8
|
|
SIE
|
1.00
|
1/1.13
|
1.13
|
0.60
|
0.44
|
2.35
|
±0.10
|
18.2
|
|
SIE
|
1.50
|
1/1.38
|
1.38
|
0.70
|
0.53
|
2.80
|
±0.15
|
12.2
|
|
SIE
|
2.50
|
1/1.78
|
1.78
|
0.80
|
0.62
|
3.40
|
±0.15
|
7.56
|