product features:
•Rated Voltage: 3000V
•Rated Temperature: -60 ℃ to +200 ℃
•Conductors: tin coated copper wire
•Insulator: Silicone Rubber
•Applicable to F, H class insulation motors and electrical appliances.
wire print:
JGG 0.75mm²～240mm² 200℃ 3000V HUA CHENG CABLE
|
ITEMS
|
Technical datas
|
Applied Standard
|
|
outer appearance
|
smooth, even, without loose
|
Q/320281ANX01-2006
GB 5013.3-1997
|
|
flame test
|
AC10KV/ 0.15 S
|
|
Vol. test
|
9 KV/5 min
|
|
Insulation machinery performance
|
before aging
|
tensile strength
|
≥5.0N/mm²
|
|
broke elongation rate
|
≥150%
|
|
after aging
|
tensile strength
|
≥4.0N/mm²
|
|
(200±3℃×240h)
|
broke elongation rate
|
≥120%
|
|
poisonous substance control
|
comply with ROHS rule
|
EU—2002/95/EC
|
|
JGG 3000V
|
|
|
spec.
|
conductor
|
insulation
|
wire OD
|
conductor resistance
|
|
structure
|
OD
|
nominal thickness
|
min. thickness
|
nominal Diameter
|
allowance
|
Ω/KM
|
|
mm²
|
No./mm
|
mm
|
mm
|
mm
|
mm
|
mm
|
below
|
|
0.75
|
24/0.20
|
1.15
|
2.0
|
1.7
|
5.15
|
±0.20
|
26.7
|
|
1.0
|
32/0.20
|
1.34
|
2.0
|
1.7
|
5.35
|
±0.20
|
20
|
|
1.5
|
30/0.25
|
1.60
|
2.2
|
1.88
|
6.0
|
±0.25
|
13.7
|
|
2.0
|
41/0.25
|
1.90
|
2.2
|
1.88
|
6.3
|
±0.25
|
9.9
|
|
2.5
|
49/0.25
|
2.0
|
2.4
|
2.06
|
6.8
|
±0.25
|
8.21
|
|
4
|
56/0.30
|
2.70
|
2.4
|
2.06
|
7.5
|
±0.25
|
5.09
|
|
6
|
84/0.30
|
3.30
|
2.6
|
2.24
|
8.5
|
±0.25
|
3.39
|
|
10
|
84/0.40
|
4.60
|
2.6
|
2.24
|
9.8
|
±0.25
|
1.95
|
|
16
|
126/0.40
|
5.80
|
2.8
|
2.42
|
11.4
|
±0.25
|
1.24
|
|
25
|
196/0.40
|
7.30
|
2.8
|
2.42
|
12.9
|
±0.30
|
0.795
|
|
35
|
276/0.40
|
8.60
|
2.8
|
2.42
|
14.2
|
±0.30
|
0.565
|
|
50
|
396/0.40
|
10.70
|
3.0
|
2.6
|
16.7
|
±0.30
|
0.393
|
|
70
|
360/0.50
|
12.40
|
3.0
|
2.6
|
18.4
|
±0.30
|
0.277
|
|
95
|
475/0.50
|
14.50
|
3.2
|
2.78
|
20.9
|
±0.40
|
0.21
|
|
120
|
608/0.50
|
16.00
|
3.2
|
2.78
|
22.4
|
±0.40
|
0.164
|
|
150
|
756/0.50
|
18.00
|
3.5
|
3.05
|
25.0
|
+0.60
|
0.132
|
|
185
|
925/0.50
|
20.00
|
3.5
|
3.05
|
27.0
|
+0.60
|
0.108
|
|
240
|
1221/0.50
|
23.00
|
3.5
|
3.05
|
30.0
|
+0.60
|
0.0817
|