product features
·Rated Voltage:600V
·Rated temperature:-60℃~+200℃
·Conductor: tin-coated, nickel-coated, silver-coated copper wire
·Insulator: silicone rubber
·Applicable for drying machine, internal leading of electrical equipment.
电线印字:E206992 UL AWM3071 3074 3075(18AWG~10AWG) 200℃ 600V CUL AWM 200℃ 600V SF-2 HUA CHENG CABLE
|
Items
|
Technical datas
|
Applied standard
|
|
Outer appearance
|
Smooth, even, without loose
|
UL 758
UL 62
UL 1581
|
|
Spark test
|
AC7.5KV/ 0.15 S
|
|
Vol. test
|
2 KV/1 min
|
|
Insulation
Machinery
Performance
|
Before aging
|
Tensile strength
|
≥3.45N/mm²
|
|
Break elongation rate
|
≥100%
|
|
After aging
|
Tensile strength
|
60% of the tensile strength before aging
|
|
(210±1℃×1440h)
|
Break elongation rate
|
25% of the elongation rate before aging
|
|
Poisonous substance control
|
Comply with ROHS rule
|
EU—2002/95/EC
|
|
TYPE
|
AWG
NO.
|
conductor
|
insulation
|
Thickness of the braid
mm
|
Wire OD
|
Conductor resistance
Ω/KM
|
|
Spec.
|
structure
No./mm
|
OD
mm
|
Nominal thickness
mm
|
Min. thickness
mm
|
OD
mm
|
Nominal diameter
mm
|
allowance
mm
|
|
AWM
3071
|
18
|
0.823
|
7/0.39
|
1.20
|
0.76
|
0.69
|
2.75
|
0.25
|
3.25
|
±0.20
|
21.8
|
|
16/0.26
|
|
16
|
1.31
|
7/0.49
|
1.47
|
0.76
|
0.69
|
3.00
|
0.25
|
3.50
|
±0.20
|
13.7
|
|
26/0.26
|
1.55
|
0.76
|
0.69
|
3.10
|
0.25
|
3.60
|
±0.20
|
|
14
|
2.08
|
7/0.62
|
1.90
|
0.76
|
0.69
|
3.45
|
0.25
|
3.95
|
±0.20
|
8.62
|
|
41/0.254
|
|
37/0.26
|
9.90
|
|
13
|
2.63
|
54/0.25
|
2.05
|
0.76
|
0.69
|
3.60
|
0.25
|
4.10
|
±0.20
|
7.60
|
|
18
|
0.823
|
1/1.05
|
1.05
|
0.76
|
0.69
|
2.60
|
0.25
|
3.10
|
±0.20
|
21.4
|
|
16
|
1.31
|
1/1.30
|
1.30
|
0.76
|
0.69
|
2.90
|
0.25
|
3.40
|
±0.20
|
13.5
|
|
1.50
|
30/0.25
|
1.60
|
0.76
|
0.69
|
3.20
|
0.25
|
3.80
|
±0.20
|
13.7
|
|
14
|
2.08
|
1/1.65
|
1.65
|
0.76
|
0.69
|
3.20
|
0.25
|
3.90
|
±0.20
|
8.45
|
|
AWM
3074
|
12
|
3.31
|
43/0.32
|
2.50
|
0.76
|
0.69
|
4.05
|
0.25
|
4.55
|
+0.30
-0.20
|
5.43
|
|
AWM
3075
|
10
|
5.261
|
35/0.45
|
3.20
|
1.15
|
1.05
|
5.50
|
0.25
|
6.00
|
+0.30
-0.20
|
3.41
|